Hard Facing

Electrode giving a weld metal with coarse chromium carbides in an austenitic matrix. Suitable for surfacing worn parts in earth-moving equipment, sand pumps, mixers, feed screws, dust extractors, crushers etc exposed to wear by coal, ores and other minerals. Also in corrosive environment and/or elevated temperature.

Stoody 134 deposit is a high chromium-iron alloy recommended for applications subject to severe abrasion, moderate impact, and high compressive loads. It can be deposited on carbon, low alloy, and manganese steel.

A general purpose hardfacing electrode depositing a semi corrosion resistant martensitic steel with a hardness of about 57 HRC. The electrode is specially suitable for hardfacing parts exposed to different forms of abrasive and impact wear, e.g. farming equipment, forestry tools, loading machines and mixers.

A hardfacing cored wire which gives Hv 550 - 650. Can be used with C1 shielding gas or self-shielded.

Stoody Super Build Up deposit is a low alloy steel that can be used both as a build-up and hardfacing material because it has good compressive strength and hardness.

‍

Stoody PR2009 is a chromium carbide wire designed specifically for the repair of worn ID claddings in pipe elbows. PR2009 is optimized to result in superior weldability for overlaying pipe ID in the horizontal position. Special deoxidizers within PR2009 make it possible to achieve sound ID claddings when repairing worn chromium carbide overlays with hydrocarbon contamination embedded in existing relief cracks.

Stoodite 6-M is the most widely used cobalt alloy with excellent resistance to many forms of mechanical and chemical degradation over a wide temperature range. Stoodite 6-M attributes include its outstanding self mated anti-galling properties, high temperature hardness, and high resistance to cavitation erosion. Certification to AWS specification - A5.21 ERCCoCr-A

ThermaClad Multipass 1 is a low alloy steel composition build-up that exhibits an excellent combination of compressive strength and toughness. Deposits are machinable, crack-free, and can be flame cut. Maximum deposit thickness is unlimited.

Bare Acetylene Tube Borium is an oxy-fuel rod intended for metal-to-earth applications involving extreme abrasion and low impact. It is manufactured by metering crushed tungsten carbide particles of controlled mesh size into steel tubes.

‍

The SOS® 430 deposit is ferritic stainless steel. This open arc wire can be used as a single layer underlay for the SOS 423 wire. The wire is specifically designed for one layer underlay on continuous caster rolls, prior to the applications of the SOS 423 overlay. The wire must not be used to deposit a final overlay on continuous caster rolls. The alloy does not require a post-weld heat treatment or temper.